Mechanical Characteristics |
Electrical Characteristics (RG6/U) |
||
|
Test Object |
Jacket |
Impedance |
75.0+/-5.0 0hmz |
|
Test Material |
PVC |
1MHz |
0.25Db |
|
Before Tensile Strength (Mpa) |
50MHz |
1.41dB |
|
|
Aging Elongation (%) > =100 |
100MHz |
1.92dB |
|
|
Aging Condition (°Cxhrs) 100x240 |
200MHz |
2.64dB |
|
|
After Tensile Strength (Mpa) >= 85% of unaged |
700MHz |
5.06dB |
|
|
Aging Elongation (%) > = 50% of unaged |
1000MHz |
6.2dB |
|
|
Cold Bend (-20±2°C x 4hrs) No Crack |
1800MHz |
8.43dB |
|
|
|
2200MHz |
9.35dB |
|
|
Electrical Characteristics |
||||||||
|
Frequency MHz |
Impedance Ohm |
RL ≥dB |
Attenuation ≤dB/100m |
NEXT ≥dB/100m |
ELFEXT ≥dB/100m |
PS NEXT ≥dB/100m |
PS ELFEXT ≥dB/100m |
NVP |
|
1 |
100 ± 15 |
20.0 |
2.0 |
65.3 |
63.8 |
62.3 |
60.8 |
17.2 |
|
4 |
23.0 |
4.1 |
56.3 |
51.7 |
53.3 |
48.7 |
||
|
8 |
24.5 |
5.8 |
51.8 |
45.7 |
48.8 |
42.7 |
||
|
10 |
25.0 |
6.5 |
50.3 |
43.8 |
47.3 |
40.8 |
||
|
16 |
25.0 |
8.2 |
47.3 |
39.7 |
44.2 |
36.7 |
||
|
20 |
25.0 |
9.3 |
48.5 |
37.7 |
42.8 |
34.7 |
||
|
25 |
24.3 |
10.4 |
44.3 |
35.8 |
41.30 |
32.8 |
||
|
31.25 |
23.6 |
11.6 |
42.9 |
33.9 |
39.9 |
30.9 |
||
|
62.5 |
21.5 |
17.0 |
38.4 |
27.8 |
35.4 |
24.8 |
||
|
100 |
20.1 |
22.0 |
35.3 |
23.4 |
20.2 |
29.4 |
||
|
150* |
100 ± 18 |
18.8 |
28.1 |
32.4 |
20.2 |
29.4 |
17.2 |
|
|
200* |
18.0 |
32.4 |
30.8 |
18.0 |
27.8 |
15.0 |
||
|
310* |
100 ± 22 |
16.7 |
41.8 |
27.9 |
14.2 |
24.9 |
11.2 |
|
|
350* |
16.3 |
44.9 |
27.1 |
13.1 |
24.1 |
10.1 |
||
* Reference values
|
Cable Construction |
|||||||
|
Part No. |
Construction |
Nominal Conductor Diameter mm |
Nominal Insulation Dimension mm |
No. of Pairs |
Nominal Cable OD mm |
Jacket |
Remarks |
|
CS512101 |
1UTP Cat. 5e + 1RG6/U |
0.51 |
0.92 |
4 |
7.2 x 13.5 |
PVC |
350MHz |
|
CS512102 |
2UTP Cat. 5e + 2RG6/U |
0.51 |
0.92 |
4 |
16.0 |
PVC |
350MHz |